The effect of graphite and slag on electrical and mechanical properties of electrically conductive cementitious composites

Electrically conductive cementitious composites (ECCCs) have become a significant research interest in structural health monitoring. The use of graphite in ECCCs can significantly improve their electrical performance, however, with unsatisfactory friction resistance because of the graphite's smooth micro-surfaces. Slag can be incorporated with graphites into ECCCs to achieve good performance in both of mechanical resistance and electrical conductivity. This study investigated the impact of graphite and slag on the electrical and mechanical behaviors of ECCCs. Two hundred and eighty ECCC specimens were prepared with two different types of slags and with various conductivity ingredient fractions and curing times. The specimens were tested for compressive strength, flexural strength, and electrical resistance. It was concluded the 4% graphite content in ECCCs can significantly enhance electrical conductivity with moderate decrease in compressive and flexural strengths. Slags were found to improve both electrical conductivity and mechanical properties of ECCCs. The best results could be obtained with optimized contents of steel slag, blast furnace slag, and graphite. Finally, the microstructural mechanisms of the ECCC specimens were analyzed using scanning electron microscope (SEM) for graphite and slag. Variable sensitivity analysis was performed to allow for optimization of ingredient contents.