Study on Mechanical Properties and Durability of Alkali-Activated Silicomanganese Slag Concrete (AASSC)

Alkali-activated materials are produced by chemically polymerizing the aluminosilicate materials using alkaline activators, which can effectively lower the greenhouse-gas emissions (approximately 73%) released by ordinary Portland cement (OPC). Silicomanganese slag is a large solid waste discharged from the ferroalloy industry in China that can pollute the environment and occupy resources. In this paper, the slag in alkali-activated material was replaced with silicomanganese slag to address the disposal of silicomangaese slag. The flowability, setting times, compressive and flexural strengths, micro-structure and freeze-thaw resistance of alkali-activated silicomanganese slag concrete (AASSC) with varied substitution ratios, volume fractions of steel fibers and alkali-activated modulus (M_S) were exploited. As a results the compressive strengths at 56 days of AASSC with a 10% substitution ratio of silicomanganese slag reached over 80 MPa and over 132 MPa with the 3% steel fiber dosage. AASSC still reached 91 MPa and 45 MPa with 60% and 100% substitution ratios by cooperating 2% steel fibers, respectively. When the freeze-thaw cycle number reached 300, the compressive strengths of AASSC with the replacement ratios of 10%, 60% and 100% were 84%, 74% and 51% of their original values by cooperating 2% steel fibers, respectively; AASSC with the numerous substitutions of 60% and 100% were destroyed at 600 and 300 freeze-thaw cycles, respectively. AASSC with a 10% substitution ratio and 2% steel fiber content is suitable for excellent performance, and a 60% substitution ratio can also be applied to construction for the massive utilization of silicomanganese slag.