Structure and magnetic properties of mechanically alloyed SmxCo1-x

J. Ding, Paul Mccormick, Robert Street

    Research output: Contribution to journalArticle

    64 Citations (Scopus)

    Abstract

    A study of the phase structure and magnetic properties of mechanically alloyed and heat-treated SmxCo1-x with x = 0.13 to 0.24 has been carried out. Remanence enhancement above 0.5 M(s) (M(s) = saturation magnetisation) was found in samples with x = 0.12 to 0.17 after annealing at 700-degrees-C. A maximum energy product of 16.6 M G Oe was measured for Sm0.13Co0.87. Coercive forces above 50 kOe were obtained for x = 0.17-0.20 after heat treatment at approximately 800-degrees-C. The highest value of 57 kOe was measured for Sm0.19Co0.81.
    Original languageEnglish
    Pages (from-to)197-201
    JournalJournal of Alloys and Compounds
    Volume191
    DOIs
    Publication statusPublished - 1993